Titel: Influence of residual stresses on the crack initiation and short crack propagation in a martensitic spring steel
AutorInn(en): Wildeis, Anna 
Christ, Hans-Jürgen 
Brandt, Robert 
Institut: Department Maschinenbau 
Schlagwörter: Fatigue crack initiation, Short fatigue crack propagation, Residual stress, Miniaturized testing device, Ermüdungsrissauslösung, Ausbreitung kurzer Ermüdungsrisse, Eigenspannung, Miniaturisierte Prüfeinrichtung
DDC-Sachgruppe: 620 Ingenieurwissenschaften und zugeordnete Tätigkeiten
GHBS-Notation: ZLQ
Erscheinungsjahr: 2022
Publikationsjahr: 2022
Auch erschienen: Metals ; 12 (7), 1085. - https://doi.org/10.3390/met12071085
Zusammenfassung: 
The crack initiation and short crack propagation in a martensitic spring steel were investigated by means of in-situ fatigue testing. Shot peened samples as well as untreated samples were exposed to uniaxial alternating stress to analyze the impact of compressive residual stresses. The early fatigue damage started in both sample conditions with the formation of slip bands, which subsequently served as crack initiation sites. Most of the slip bands and, correspondingly, most of the short fatigue cracks initiated at or close to prior austenite grain boundaries. The observed crack density of the emerging network of short cracks increased with the number of cycles and with increasing applied stress amplitudes. Furthermore, the prior austenite grain boundaries acted as obstacles to short crack propagation in both sample conditions. Compressive residual stresses enhanced the fatigue strength, and it is assumed that this beneficial effect was due to a delayed transition from short crack propagation to long crack propagation and a shift of the crack initiation site from the sample surface to the sample interior.
Beschreibung: 
Finanziert aus dem Open-Access-Publikationsfonds der Universität Siegen für Zeitschriftenartikel
DOI: http://dx.doi.org/10.25819/ubsi/10179
URN: urn:nbn:de:hbz:467-22687
URI: https://dspace.ub.uni-siegen.de/handle/ubsi/2268
Enthalten in den Sammlungen:Publikationen aus der Universität Siegen

Diese Ressource ist urheberrechtlich geschützt.

Zur Langanzeige

Seitenansichten

9
checked on 26.09.2022

Download(s)

1
checked on 26.09.2022

Google ScholarTM

Prüfe

Prüfe


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt, soweit nicht anderweitig angezeigt.